metal

nano-varnish

dry-film-thickness in microns

gloss

corrosion protection

crockmeter test6

taber-abraser test7

contact angle water

contact angle hexadecane

anti-fingerprint

remarks

condensation-water constant climate3

neutral salt spray test4

filiform corrosion protection test5

steel1 without conversion layer

without

- 55 %

- 43 %

85°

H 1172

> 10

80°

30°

insulating varnish

H 5055

1 - 2

glossy

480 h

< 24 h

- 3 %

- 1 %

> 105°

> 65°

H 5220

1 - 2

glossy

480 h

< 24 h

- 1 %

> 105°

> 65°

H 5396

2 - 3

silk-matt

- 4 %

- 3 %

> 105°

> 65°

curing at ambient temperature

M 0046

10 - 20

glossy

480 h

250 h

- 15 %

85°

35°

M 0049

10 - 20

glossy

480 h

250 h

- 10 %

100°

50°

M 0060

8 - 12

glossy

480 h

250 h

- 20 %

> 105°

> 60°

steel1 elektrolytically galvanized

M 0046

19

glossy

1200 h

aluminium2

without

- 20 %

- 70 %

100°

H 5055

1 - 2

high gloss

1000 h

1000 h

168 h

- 3 %

- 22 %

> 105°

> 65°

H 5179

2 - 4

high gloss

1000 h

- 3 %

- 20 %

> 105°

> 65°

H 5220

2 - 4

high gloss

1000 h

1000 h

1000 h

- 28 %

> 105°

> 65°

H 5294

5 - 10

glossy

1000 h

1000 h

1000 h

> 105°

> 65°

beadable

H 5396

2- 3

silk-matt

- 5 %

- 2 %

> 105°

> 65°

curing at ambient temperature

M 0046

15 - 20

glossy

1000 h

1000 h

- 20 %

- 45 %

70°

35°

M 0049

10 - 20

glossy

1000 h

1000 h

- 25 %

- 50 %

100°

50°

M 0060

11  14

glossy

1000 h

1000 h

- 25 %

> 105°

> 60°

aluminium2 with Primer H 1068

M 0040

glossy

1000 h

- 25 %

90°

20°

copper

without

- 20 %

- 64 %

95°

H 5055

1 - 2

high gloss

- 1 %

- 4 %

> 105°

> 65°

tarnish protection

H 5164

1 - 2

high gloss

- 2 %

> 105°

> 65°

tarnish protection

H 5346

1 - 2

high gloss

- 5 %

> 105°

> 65°

tarnish protection, curing at ambient temperature

brass

without

- 57 %

90°

H 5055

1 - 2

high gloss

- 12 %

- 5 %

> 105°

> 65°

tarnish protection

H 5164

1 - 2

high gloss

- 5 %

> 105°

> 65°

tarnish protection

H 5346

1 - 2

high gloss

- 15 %

> 105°

> 65°

tarnish protection, curing at ambient temperature

stainless steel

without

100°

H 1172

> 10

glossy

80°

30°

insulating varnish

H 5055

1 - 2

high gloss

- 2 %

- 14 %

> 105°

> 65°

H 5270

2 - 3

high gloss

0 %

> 105°

> 65°

H 5103

2 - 3

silk-matt

0 %

> 105°

> 65°

¹ =  DC 01
² = AlMnCu1
³ = DIN EN ISO 6270-2
⁴ = DIN EN ISO 9227
⁵ = according to DIN EN ISO 4623
⁶ = gloss change (at 20°) in % after 10 double strokes,  with 9 µm rough film, at a loading rate of 9N
⁷ = gloss change in %,  50 cycles