Product recommendation for plastics coating

plastics
nano-varnishdry film thickness in micronscrockmeter test1scratch resistance2Taber Abraser3contact angle watercontact angle hexadecaneanti-fingerprintremarks
PET

without -70 %< 6B88°- 
H 5112 1-20 %HB> 105°> 65°with ketones as solvent
H 5120 1-20 %HB> 105°> 65°with alcohols as solvent
PMMA



without -25 %H-50 %85°- 
H 5112 1-20 %4H> 105°> 65°with ketones as solvent
H 5129 1-20 %6H> 105°> 65°with alcohols as solvent
H 5270 1-2-1 %5H-8 %> 105°> 65°with alcohols as solvent
H 5271  1-2-2 %5H-8 %> 105°> 65°with alcohols as solvent, VOC reduced
PC



without -40 %5B-90 %89°- 
H 5112 1-2-1 %3H> 105°> 65°with ketones as solvent
H 5120 1-21 %F-22 %> 105°> 65°with alcohols as solvent
H 5270 1-21 %2H-20 %> 105°> 65°with alcohols as solvent
H 5271 1-20 %H-10 %> 105°> 65°with alcohols as solvent, VOC reduced
ABSwithout-93 %3B82°15°  
H 5112 1-2-2 %H> 105°> 65°with ketones as solvent
H 5120 1-20 %H> 105°> 65°with alcohols as solvent

PA 6

(white)

without -82 %2B73°- 
H 5120 1-20 %3H> 105°> 65°with alcohols as solvent
H 5143 1-20 %3H> 105°> 65°with alcohols as solvent

PVC

(grey)

without -16 %3H80°20° 
H 5112 1-20 %3H> 105°> 65°with ketones as solvent
H 5120 1-2-1 %3H> 105°> 65°with alcohols as solvent

 HDPE

(black)

without -72 %< 6B103° 17° 
H 5044 1-2-1 %4B> 105°> 65°with alcohols as solvent
H 5218 2-3-22 %4B> 105°> 65°with alcohols as solvent, corundum, opaque

1 = gloss change (at 20°) in % after 10 double strokes, with 9 µm rough film, at a loading rate of 9N
2 = pencil hardness according to ISO 1584
3 = gloss change in %, 100 cycles